In normal cases UV stabilizer is mixed externally as par the requirement of the product before injection molding.
PET is made chemically by pure terephthalic acid and ethylene glycol.It can be made either homopolymer or copolymer. For copolymer either it is modified by CHDM (glycol modified) or by Isophthalic acid (Acid modified.)through polycondensation reaction.

Fine
1
Poor
12/27/2006 1:05:53 PM By Chandranath Dutta
Hello,please could you give us the chemical composition of PET bottles (if uv stabilizer is used)? and what are the causes of changing the water taste ?

Fine
2
Poor
11/22/2006 3:47:16 AM By Bassam Reaidy
we are about to establish water bottling plant . what would be the full specifications of PET bottles should be choosen for the process

Fine
Poor
11/5/2006 3:19:37 PM By mohammed
Not only the direct heat through barrel , indirect heat or frictional heat by means of screw RPM , B.P, screw speed and melt residence time along with larger cushion generating AA.
Should try our ASPET 19C material for making water grade bottles.

Fine
Poor
8/24/2006 7:36:57 PM By Chandranath Dutta
1. AA level too high. Apply lower temperature for both injection and blowing;
2. Choose PET resin with lower AA level.

Fine
Poor
2/15/2006 4:05:31 PM By Kenplas
1
 
 

Post A Reply

Temporarily shut down, no new message, sorry.

Name:

Email:

Message:

(Max. 2KB)



Attachment:     (Max. 500kB, .RAR.ZIP.JPG.GIF only)
Verification:

This forum published since July 03, 2002. Renewed on June 22, 2005.

[Plastics Project] [Plastics Machinery] [Plastics Mold] [Discussion Forum] [Contact Kenplas]
Copyright © 2017 Kenplas Industry Limited, Hangzhou Kenplas Machinery Ltd.              Powered by Alentus.